dc.description.abstract | This research was conducted to synthesize TiO2 nanotubes to determine the
effect of stirring times during the hydrothermal process. TiO2 nanotubes were
synthesis by one-step hydrothermal process from TiO2 micropowder as a
precursor. TiO2 micropowder was mixed with 10 M NaOH and treated
hydrothermally at 130 °C in an autoclave for 24 hours with stirring. The
variations of stirring time that have been used are 10, 15 and 20 minutes/hour.
The synthesized TiO2 nanotube were characterized using SEM, TEM, XRD, SAA,
and UV-Vis DRS. The synthesized TNT was applied as photocalyst in degrading
diazinon compounds. The results of this study indicate that TNT has the form of a
fiber with particle sizes ranging from 12-69 nm. The tubular structure of TNT was
observed by TEM has inner, outer, and thickness with 3.31 nm, 6.15 nm and 1,64
nm. TNT 15 minutes/hour has anatase with high crystallinity. Sodium titanate was
detected in the TNT 10 minutes/hour and TNT 20 minutes/hour. The surface area
increases with increasing sodium titanate content in the sample. Furthermore, a
small pore size results in a large surface area and total pore volume. The
photocatalytic activity of TNT was carried out on the organic pollutant diazinon
with variations of irradiation. The optimum conditions for the TNT photocatalytic
in this study were observed in the TNT 20 minutes/hour, which showed 90%
diazinon degradation during 210 minutes of irradiation. | en_US |
dc.language.iso | other | en_US |
dc.publisher | Fakultas Matematika dan Ilmu Pengetahuan Alam | en_US |
dc.subject | TiO2 Nanotubes | en_US |
dc.subject | DIAZINON | en_US |
dc.subject | HYDROTHERMAL | en_US |
dc.subject | PHOTOCATALYSIS | en_US |
dc.subject | STIRRING TIME | en_US |
dc.title | Sintesis TIO2 Nanotube Menggunakan Metode Hidrotermal dengan Variasi Waktu Pengadukan Terhadap Aktivitas Fotokatalitik Senyawa Diazinon | en_US |
dc.type | Skripsi | en_US |
dc.identifier.prodi | Kimia | en_US |
dc.identifier.pembimbing1 | Novita Andarini, S.Si., M.Si. | en_US |
dc.identifier.pembimbing2 | Tanti Haryati, S.Si., M.Si. | en_US |
dc.identifier.validator | validasi_repo_iswahyudi_Mei_2024 | en_US |
dc.identifier.finalization | Taufik | en_US |